| Nano-DURASIL |
|
unmodified nano silica layers for HPTLC
|
|
|
Features
|
|
|
nano silica 60, specific surface (BET) ~ 500 m2/g, mean pore size 60 Å, specific pore volume 0.75 ml/g,
particle size 2 – 10 µm
indicator: manganese activated zinc silicate with green fluorescence for short-wave UV (254 nm)
hard, water-resistant and wettable layers due to a special binder system
narrow fractionation of the silica particles allows sharper separations, shorter developing times, shorter migration distances, smaller samples and an increased detection sensitivity compared to DURASIL plates
different selectivity compard to ADAMANT and SIL-G plates
no reversed phase tendency, more polar than SIL-G
available as glass plates with or without fluorescent indicator
|
|
for applications on Nano-DURASIL plates click here:  |
Ordering information
Designation
|
Thickness of layer
|
Plate size
|
Fluorescent indicator
|
Plates per pack
|
REF
|
|
Glass plates
|
| Nano-DURASIL-20 |
0.20 mm |
10 x 10 cm
|
–
|
25
|
812010
|
|
| Nano-DURASIL-20 |
0.20 mm |
10 x 20 cm
|
–
|
50
|
812011
|
|
| Nano-DURASIL-20 UV254 |
0.20 mm |
5 x 5 cm
|
UV254 |
100
|
812012
|
|
| Nano-DURASIL-20 UV254 |
0.20 mm |
10 x 10 cm
|
UV254 |
25
|
812013
|
|
| Nano-DURASIL-20 UV254 |
0.20 mm |
10 x 20 cm
|
UV254 |
50
|
812014
|
|
|
|
|
|
|
|
|
|
 |
|
|
 |